Alkaline hydrothermal treatment of brominated high impact polystyrene [An article from: Chemosphere]
Book Details
Author(s)
M. Brebu, T. Bhaskar, A. Muto, Y. Sakata
Publisher
Elsevier
ISBN / ASIN
B000P6O6MM
ISBN-13
978B000P6O6M0
Availability
Available for download now
Marketplace
United States 🇺🇸
Description
This digital document is a journal article from Chemosphere, published by Elsevier in 2006. The article is delivered in HTML format and is available in your Amazon.com Media Library immediately after purchase. You can view it with any web browser.
Description:
A method to recover both Br and Br-free plastic from brominated flame retardant high impact polystyrene (HIPS-Br) was proposed. HIPS-Br containing 15% Br was treated in autoclave at 280^oC using water or KOH solution of various amounts and concentrations. Hydrothermal treatment (30ml water) leads to 90% debromination of 1g HIPS-Br but plastic is strongly degraded and could not be recovered. Alkaline hydrothermal treatment (45ml or 60ml KOH 1M) showed similar debromination for up to 12g HIPS-Br and plastic was recovered as pellets with molecular weight distribution close to that of the initial material. Debromination occurs at melt plastic/KOH solution interface when liquid/vapour equilibrium is attained inside autoclave (280^oC and 7MPa in our experimental conditions) and depends on the plastic amount/KOH volume ratio. The antimony oxide synergist from HIPS-Br remains in recovered plastic during treatment. A pictorial imagination of the proposed debromination process is presented.
Description:
A method to recover both Br and Br-free plastic from brominated flame retardant high impact polystyrene (HIPS-Br) was proposed. HIPS-Br containing 15% Br was treated in autoclave at 280^oC using water or KOH solution of various amounts and concentrations. Hydrothermal treatment (30ml water) leads to 90% debromination of 1g HIPS-Br but plastic is strongly degraded and could not be recovered. Alkaline hydrothermal treatment (45ml or 60ml KOH 1M) showed similar debromination for up to 12g HIPS-Br and plastic was recovered as pellets with molecular weight distribution close to that of the initial material. Debromination occurs at melt plastic/KOH solution interface when liquid/vapour equilibrium is attained inside autoclave (280^oC and 7MPa in our experimental conditions) and depends on the plastic amount/KOH volume ratio. The antimony oxide synergist from HIPS-Br remains in recovered plastic during treatment. A pictorial imagination of the proposed debromination process is presented.